Corrosion inhibiting admixture for concrete
BATIMIX Anti-Corrosion 622 is a calcium nitrate liquid admixture that inhibits corrosion of steel reinforcements embedded in concrete. It is blended with set-retarding chemicals to offset any acceleration that may occur due to calcium nitrate.
In normal circumstances, the high alkalinity of concrete leads to the formation of a passivating layer that protects steel rebars from corrosion. However, such a passive ferric oxide layer may be damaged by the presence of chlorides, which damage when combined with moisture and oxygen results in cracking, spalling, and failure of concrete structural elements.
BATIMIX Anti-Corrosion 622 is designed to chemically oxidise the steel to inhibit corrosion and rust formation. When used at recommended dosage rates, it prevents ferrous chloride complex formation by reacting with defective ferrous oxide ions prior to chloride attack, reforming the passivating layer. Nitrate ions surround the defective ferrous oxide ions and convert them to more stable ferric ion species less susceptible to corrosion.
BATIMIX Anti-Corrosion 622 is applied to new cast and repaired structures that are potentially vulnerable to corrosion. These include steel-reinforced, precast, pre-stressed, and post-tensioned concrete.
Concrete prepared with BATIMIX Anti-Corrosion 622 is characterized by the following:
In the plastic state:
In the hardened state:
1% to 6% of the cement weight
light brown liquid